Abstract: Ensure that the gas insulated switchgear (GIS) used in epoxy casting insulating parts stable and reliable performance is the primary control goal of the insulating parts. For epoxy casting with raw materials, put forward epoxy resin, filler, curing agent basic must test project type, in order to control the stability of raw material performance, and in the epoxy casting with epoxy, filler, curing agent basic test project, it is proposed to increase infrared spectroscopy, molecular weight distribution of the two project testing, through the basic must test project and the proposal to increase the test project, to stabilize the quality of the epoxy casting insulation parts, and to enhance the safety of the GIS.
Key words: gas insulated switchgear; epoxy casting; insulation; infrared spectroscopy; molecular weight distribution
參考文獻(xiàn)
[1] 武奇，袁志兵，孫榮春，等.252kV SF6/N2 混合氣體 GIS 用盆式絕緣子的設(shè)計研究[J] . 電工電氣，2023(5) ：58-62.
[2] 袁志兵，孫榮春，李保朋，等. X 射線檢測在環(huán)氧澆注絕緣件生產(chǎn)中的應(yīng)用[J] . 上海電氣技術(shù)，2024，17(2) ：32-36.
[3] 王光明，王建偉，吳薇，等. 影響環(huán)氧澆注性能因素研究[J]. 科技視界，2018(26) ：38-40.
[4] 陸煜. 液體成型用環(huán)氧樹脂/酸酐體系催化固化反應(yīng)與性能研究[D]. 哈爾濱：哈爾濱工業(yè)大學(xué)，2023.
[5] 費龍菲，張建宏，王光明. 環(huán)氧樹脂固化物耐開裂因素的研究[J]. 絕緣材料通訊，1997(4) ：31-34.
[6] 王光明，周清政，張輝. 環(huán)氧澆注絕緣子檢測方法研究[J]. 上海電氣技術(shù)，2019，12(3) ：33-37．
[7] 顏晨光，劉宏斌，王光明. 發(fā)電機(jī)斷路器絕緣子用高性能環(huán)氧樹脂材料國產(chǎn)化研究[J] . 絕緣材料，2019，52(6) ：17-20．
[8] 胡賢飛. 超支化環(huán)氧樹脂的合成及改性環(huán)氧/酸酐固化體系研究[D]. 無錫：江南大學(xué)，2022.
[9] 曾慶忠，王光明，朱琦，等. 環(huán)氧澆注自動壓力凝膠工藝在 GIS 用電流互感器上的應(yīng)用[J] . 科技視界，2018(33) ：139-141.
[10] 李建忠. 氧化鋁性能對環(huán)氧澆注的影響[J]. 中國粉體技術(shù)，2005，11(4) ：47-49.
[11] 許春. 多通道原位紅外光譜在粘結(jié)劑反應(yīng)動力學(xué)中的應(yīng)用研究[D]. 綿陽：西南科技大學(xué)，2023.
[12] 王傳川，牛建鴻，王光明，等. 環(huán)氧澆注設(shè)備組成及其影響分析[J]. 設(shè)備監(jiān)理，2021(2) ：37-43.
[13] 張國寶，楊為，黃偉民, 等. X 射線輻照對 GIS 用環(huán)氧絕緣材料性能的影響[J] . 高電壓技術(shù)，2025，51(3) ：1380-1388.